Product Description
Injection Alloy Filament
The ERYONE Alloy Filament is a high-performance composite material made from a
combination of PC and ABS. It offers excellent heat resistance, high toughness, low odor, impact
resistance, and printing stability, with a heated bed temperature requirement of only 70°C and a
tensile strength of approximately 23MPa. Its high precision and low warping characteristics make
it ideal for printing high-strength mechanical parts such as gears and screws, particularly suitable
for functional part manufacturing in high-temperature environments. It is a high-quality 3D
printing material that balances performance and ease of use.
Part I:Suggests Printing Parameters
| Parameter | Set up |
| Nozzle temperature | 240-260 ℃ |
| Bed temperature | 70-80℃ |
| Bed materia | glass, PEI, spring steel plate |
| Bottom printing temperature | 250-260 ℃ |
| Sealed printing | Supports open printing; better results with enclosure. |
| Printing speed | 30-300mm/s |
| Drying conditions | 70-80℃, 12h |
Part II: Physical Properties of Materials
| Property | Testing Method | Unit | Typical Value |
| Density(g/cm³ at 21.5 ° C） | ASTM D792 (ISO 1183, GB/T 1033) | g/cm³ | 1.05-1.11 |
|
Water absorption rate
|
ASTM D750
|
%
|
<0.7
|
| Heat distortion temperature(° C) | ASTM D648 1.8MPa 0.45MPa | ℃ | 65-67 |
|
Melt Index(g/10 min)
|
220 ° C, 10kg 240 ° C, 2.16 kg
|
g/10min
|
17-23
|
Part III: Mechanical Properties of Printed Samples
| Property | Test conditions | Test standards | unit | Typical Value |
| Tensile strength X-Y | 50mm/min | GB/T 1040.4 | MPa | 37.2 |
| Elastic modulus X-Y | 50mm/min | GB/T 1040.1-2006 | MPa | 1532.9 |
| Elongation at break X-Y | 50mm/min | GB/T 1040.4 |
MPa
|
4.5 |
| Tensile strength X-Z | 50mm/min | GB/T 1843 | MPa | 22.3 |
| Elastic modulus X-Z | 50mm/min | GB/T 1040.1-2006 | MPa | 1375.3 |
| Elongation at break X-Z | 50mm/min | GB/T 1040.4 | % | 3.2 |
| Bending strength | 2mm/min | GB/T 9341 | MPa | 52.8 |
| Bending modulus | 2mm/min | GB/T 9341 | MPa | 1857.1 |
| Charpy Impact strenght | 2.75J | GB/T 1843 | kJ/m2 | 14.3 |
Note: All splines are printed under the following conditions: printing temperature=260 ° C, printing speed=80mm/s, base plate 70° C, filling=100%, nozzle diameter=0.4mm